Differential Biodegradation Kinetics of Collagen Membranes for Bone Regeneration

Native collagen-based membranes are used to guide bone regeneration; but due to their rapid biodegradation, this treatment is often unpredictable. The purpose of this study was to investigate the biodegradability of natural collagen membranes. Three non-cross-linked resorbable collagen barrier membr...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Polymers 2020-06, Vol.12 (6), p.1290
Hauptverfasser: Toledano, Manuel, Asady, Samara, Toledano-Osorio, Manuel, García-Godoy, Franklin, Serrera-Figallo, María-Angeles, Benítez-García, José A., Osorio, Raquel
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Native collagen-based membranes are used to guide bone regeneration; but due to their rapid biodegradation, this treatment is often unpredictable. The purpose of this study was to investigate the biodegradability of natural collagen membranes. Three non-cross-linked resorbable collagen barrier membranes were tested: Derma Fina (porcine dermis), Evolution Standard (equine pericardium) and Duo-Teck (equine lyophilized collagen felt). 10 × 10 mm2 pieces of membranes were submitted to three different degradation procedures: (1) hydrolytic degradation in phosphate buffer solution, (2) enzyme resistance, using a 0.25% porcine trypsin solution, and (3) bacterial (Clostridium histolyticum) collagenase resistance test. Weight measurements were performed with an analytic microbalance. Thickness was measured with a digital caliper. Membranes were analyzed at different time-points, up to 21 d of immersion. A stereomicroscope was used to obtain membranes’ images. ANOVA and Student Newman Keuls were used for mean comparisons (p < 0.05), except when analyzing differences between time-points within the same membrane and solution where pair-wise comparisons were applied (p < 0.001). Derma Fina attained the highest resistance to all degradation challenges. Duo-Teck was the most susceptible membrane to degradation, complete degradation occurred as soon as 8 h. The bacterial collagenase solution performed as the most aggressive test as all membranes presented 100% degradation before 21 d.
ISSN:2073-4360
2073-4360
DOI:10.3390/polym12061290