In Situ Ternary Boride: Effects on Densification Process and Mechanical Properties of WC-Co Composite Coating

New coatings resistant to corrosion in high-temperature molten zinc aluminum were prepared by supersonic flame spraying of various composite powders. These composite powders were prepared by mixing, granulation, and heat treatment of various proportions of Mo-B C powder and WC and Co powder. X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), energy dispersive X-ray spectroscopy (EDS), and mechanical analysis were used to study the effects of Mo-B C on the microstructure, phase, porosity, bonding strength, and elastic modulus of the composite powder and coating. Results show that the addition of an appropriate quantity of Mo-B C reacts with Co to form ternary borides CoMo B and CoMoB. Ternary boride forms a perfect continuous interface, improving the mechanical properties and corrosion resistance property of the coating. When the amount of Mo-B C added was 35.2%, the mechanical properties of the prepared coating reached optimal values: minimum porosity of 0.31 ± 0.15%, coating bonding strength of 77.81 ± 1.77 MPa, nanoindentation hardness of 20.12 ± 1.85 GPa, Young's modulus of 281.52 ± 30.22 GPa, and fracture toughness of 6.38 ± 0.45 MPa·m .