Poly(tris(4-carbazoyl-9-ylphenyl)amine)/Three Poly(3,4-ethylenedioxythiophene) Derivatives in Complementary High-Contrast Electrochromic Devices

A carbazole-based polymer (poly(tris(4-carbazoyl-9-ylphenyl)amine) (PtCz)) is electrosynthesized on an indium tin oxide (ITO) electrode. PtCz film displays light yellow at 0.0 V, earthy yellow at 1.3 V, grey at 1.5 V, and dark grey at 1.8 V in 0.2 M LiClO₄/ACN/DCM (ACN/DCM = 1:3, by volume) solution. The Δ and coloration efficiency ( ) of PtCz film are 30.5% and 54.8 cm²∙C , respectively, in a solution state. Three dual-type electrochromic devices (ECDs) are fabricated using the PtCz as the anodic layer, poly(3,4-ethylenedioxythiophene) (PEDOT), poly(3,3-dimethyl-3,4-dihydro-thieno[3,4- ][1,4]dioxepine) (PProDOT-Me₂), and poly(3,4-(2,2-diethylpropylenedioxy)thiophene) (PProDOT-Et₂) as the cathodic layers. PtCz/PProDOT-Me₂ ECD shows high Δ (36%), high (343.4 cm²·C ), and fast switching speed (0.2 s) at 572 nm. In addition, PtCz/PEDOT, PtCz/PProDOT-Me₂, and PtCz/PProDOT-Et₂ ECDs show satisfactory open circuit memory and long-term stability.