Optimizing mechanical properties of Fe26.7Co26.7Ni26.7Si8.9B11 high entropy alloy by inducing hypoeutectic to quasi-duplex microstructural transition

High-entropy alloys (HEAs) have inspired considerable interest due to their attractive physical and mechanical properties. In this work, the microstructural evolution induced by different heat treatments on rapidly solidified hypoeutectic precursors of a Fe 26.7 Co 26.7 Ni 26.7 Si 8.9 B 11 HEA is investigated and correlated with the corresponding mechanical properties. The microstructures of the rapidly solidified precursors are composed of primary fcc solid solution dendrites embedded in a eutectic matrix. When the samples are annealed at different temperatures after furnace cooling or quenching, respectively, the eutectic structure gradually decomposes into fcc , tetragonal (Fe,Co) 2 B, and hexagonal Ni 31 Si 12 crystals with increasing annealing temperature, leading to a gradual increase of the content of the fcc crystals and both their aggregation and coarsening. Then the dominant structural framework gradually transforms from eutectic structures to fcc dendrites and ultimately the (Fe,Co) 2 B crystals become isolated as dominant reinforcement particles distributed in the interdendritic regions. This gradual microstructural transition from hypoeutectic to quasi-duplex structures leads to the change of the dominant deformation mechanism from crack-controlled to dislocation-dominated deformation, which allows to control both ductility and strength in a wide range. Hence, this study provides some guideline for how to tune the microstructure and mechanical properties of HEAs.