Different Setting Conditions Affect Surface Characteristics and Microhardness of Calcium Silicate-Based Sealers

Objective. To investigate the effect of different setting conditions on surface microhardness and setting properties of calcium silicate-based sealers. Methods. Three sealers, EndoSequence Bioceramic (BC; Brasseler USA, Savannah, GA, USA), Endoseal MTA (ES; Maruchi, Wonju, Korea), and Well-Root ST (WR; Vericom, Chuncheon, Korea), were compared. Specimens were exposed to either butyric acid (pH 5.4) or phosphate-buffered saline (PBS [pH 7.4]) for 48 h and stored at 100% humidity for 12 days. The control specimens were stored at 100% humidity for 14 days. Surface microhardness was measured, topographic changes were observed, and phase analysis was performed using X-ray diffraction. Microhardness according to storage conditions was compared using one-way analysis of variance and Tukey’s multiple comparison tests (P