Effects of Different Percentages of Microhydroxyapatite on Microhardness of Resin-modified Glass-ionomer and Zirconomer

Hydroxyapatite (HA) is the main mineral component of the tooth structure, which exhibits considerable biological behavior and its incorporation might improve microhardness of dental materials. Microhardness of restorative materials, like glass-ionomer, is critical for the clinical longevity of restorations. The aim of this study was to evaluate the microhardness of two glass-ionomers types by incorporating different percentages of microhydroxyapatite. In this study, 80 disc-shaped experimental specimens (6 mm in diameter, 2 mm in height) were prepared in 8 groups, including resin-modified glass-ionomer (RMGI, GC, Gold Label, Japan), zirconia-reinforced glass-ionomer (Zirconomer, Shofu, Kyoto, Japan), and their mixture with 0, 5, 15 and 25 wt% of microhydroxyapatite (Sigma-Aldrich, Germany). All the specimens were stored in deionized water at 37ºC for 24 hours. Then Vickers microhardness test was carried out on the both sides of specimens and data were analyzed using two-way ANOVA and paired t-test (