Preclinical evaluation of a novel abluminal surface coated sirolimus eluting stent with biodegradable polymer matrix

Second generation of drug eluting stents (DES) has attempted to improve safety using abluminal sirolimus drug delivery with biodegradable polymers matrix. The present preclinical study was designed to investigate the safety and efficacy profile of Abluminus™ stents (SES). This is a new coronary stent with sirolimus and biodegradable polymer matrix coated on abluminal stent and balloon surface. SES were compared with two controls: bare metal stent (BMS) and BMS + polymer coated stents (PC). All devices (40 stents) were implanted in porcine coronary arteries with primary endpoint of endothelialization at 7 days and subsequent histological and morphometric evaluations at 7, 30 and 90 days. Early endothelialization at seven days was complete in all stents. Histology at 30 days revealed minimum inflammation in all groups and increased at 90 days in PC group while it was absent at 180 days. Thirty day morphometry showed significantly reduction of neointimal area in Abluminus™ (SES 0.96±0.48 mm(2); BMS 1.83±0.34 mm(2); PC 1.76±0.55 mm(2); P