SLM Magnesium Alloy Micro-Arc Oxidation Coating

In this study, we utilized Selective Laser Melting (SLM) technology to fabricate a magnesium alloy, and subsequently subject it to micro-arc oxidation treatment. We analyzed and compared the microstructure, elemental distribution, wetting angle, and corrosion resistance of the SLM magnesium alloy both before and after the micro-arc oxidation process. The findings indicate that the SLM magnesium alloy exhibits surface porosity defects ranging from 2% to 3.2%, which significantly influence the morphology and functionality of the resulting film layer formed during the micro-arc oxidation process. These defects manifest as pores on the surface, leading to an uneven distribution of micropores with varying sizes across the layer. The surface roughness of the 3D-printed magnesium alloy exhibits a high roughness value of 180 nanometers. The phosphorus (P) content is lower within the film layer compared to the surface, suggesting that the Mg (PO ) phase predominantly resides on the surface, whereas the interior is primarily composed of MgO. The micro-arc oxidation process enhances the hydrophilicity and corrosion resistance of the SLM magnesium alloy, thereby potentially endowing it with bioactivity. Additionally, the increased surface roughness post-treatment promotes cell proliferation. However, certain inherent defects present in the SLM magnesium alloy samples negatively impact the improvement of their corrosion resistance.