Comparative analysis of an epoxy resin-based and a premixed calcium silicate-based sealer's push-out bond strength with and without incorporation of chitosan nanoparticles: An in vitro investigation

The aim of the study was to compare and evaluate the push-out bond strength (POBS) of epoxy resin-based and calcium silicate-based sealers with and without incorporating chitosan nanoparticles (CSNPs). Eighty human mandibular premolars with a single canal were taken. A standard root length of 15 mm was established. Canals were instrumented with Neoendo files up to size 30, 4% and were irrigated with 5 ml of 2.5% NaOCl, and 5 ml of ethylenediaminetetraacetic acid 17%. Then, samples were obturated using the size 30, 4% gutta-percha, single-cone technique using respective sealers. For POBS, it was grouped as Group 1 Adseal, Group 2 CeraSeal, Group 3 Adseal + 2% wt/vol CSNP, and Group 4 CeraSeal + 2% wt/vol CSNP. Samples embedded in acrylic resin were sectioned transversely at 11 and 7 mm from the apex. Dislodgment resistance was calculated using a universal testing machine. The data were analyzed using a one-way ANOVA test, followed by Tukey's analysis. The level of significance ( value) was set at < 0.05. At 7 mm from the apex, Group 4 (CeraSeal + 2% wt/vol CSNP) demonstrated significantly higher mean POBS. However, no significant difference was observed between Groups 1 (Adseal), Group 2 (CeraSeal), and Group 3 (Adseal + 2% wt/vol CSNP). At 11 mm from the apex, Group 2 (CeraSeal) and Group 4 (CeraSeal + 2% wt/vol CSNP) demonstrated significantly higher mean POBS. On comparison between POBS at 7 mm and 11 mm from the apex, the mean POBS at the 11 mm region from the apex was significantly higher in all study groups, which was statistically significant. Within the limitations of the study, it has been concluded that Group 4 (CeraSeal + 2% wt/vol CSNP) has better bond strength compared to the other groups.