Relationship between Texture, Hydrogen Content, Residual Stress and Corrosion Resistance of Electrodeposited Chromium Coating: Influence of Heat Treatment

Electrodeposited chromium plating continues to be widely used in a number of specialized areas, such as weapons, transport, aerospace, etc. However, the formation of texture, hydrogen content and residual stress can degrade the serviceability and lead to material failure. The effect of post heat treatment processes on the relationship of texture, hydrogen content, residual stress and corrosion resistance of hexavalent [Cr(VI)] chromium coatings deposited on Cr-Ni-Mo-V steel substrates was investigated. Macrotexture was measured by XRD. Microtexture, dislocation density and grain size were studied by EBSD. With the increase of the heat treatment temperature, it was found that the fiber texture strength of the (222) plane tended to increase and subsequently decrease. Below 600 °C, the increase in the (222) plane texture carried a decrease in the hydrogen content, residual stress, microhardness and an increase in the corrosion resistance. In addition, crack density and texture strength were less affected by the heat treatment time. Notably, relatively fewer crack densities of 219/cm , a lower corrosion current density of 1.798 × 10 A/dm and a higher microhardness of 865 HV were found under the preferred heat treatment temperature and time of 380 °C and 4 h, respectively. The hydrogen content and residual stress were 7.63 ppm and 61 MPa, with 86% and 75% reduction rates compared to the as-plated state, respectively. In conclusion, in our future judgement of the influence of heat treatment on coating properties, we can screen or determine to a certain extent whether the heat treatment process is reasonable or not by measuring only the macrotexture.