Long-Cycle Stability of In Situ Ultraviolet Curable Organic/Inorganic Composite Electrolyte for Solid-State Batteries

Lithium-ion solid-state batteries with spinel Li Ti O (LTO) electrodes have significant advantages, such as stability, long life, and good multiplication performance. In this work, the LTO electrode was obtained by the atmospheric plasma spraying method, and a composite solid electrolyte was prepared by in situ ultraviolet (UV) curing on the LTO electrode. The composite solid electrolyte was designed using a soft-hard combination strategy, and the electrolyte was prepared into a composite of a poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) flexible structure and high-conductivity Li Al Ti (PO ) (LATP) hard particles. The composite electrolyte exhibited a good ionic conductivity up to 0.35 mS cm at 30 °C and an electrochemical window above 4.0 V. In situ and ex situ electrolytes were assembled into LTO//electrolyte//Li solid-state batteries to investigate their impact on the electrochemical performance of the batteries. As a result, the assembled Li Ti O //in situ electrolytes//Li batteries exhibited excellent rate of performance, and their capacity retention rate was 90% at 0.2 mA/cm after 300 cycles. This work provides a new method for the fabrication of novel advanced solid-state electrolytes and electrodes for applications in solid-state batteries.