The Influences of Ultrasonic Vibrations on Laser Cladding Ni60/WC-TiO2+La2O3 Composite Coating

The optimal process parameters of ultrasonic-assisted processing were studied to further improve the molding quality and mechanical properties of Ni60/WC-TiO2+La2O3 composite coating. A single-factor experiment was used to explore the influences of ultrasonic vibration frequencies on Ni60/WC-TiO2+La2O3 composite coating. The microstructure, elemental composition, phase composition, hardness, and wear resistance of the coating were studied using scanning electron microscopy (SEM), an X-ray diffractometer (XRD), an energy spectrometer, a microhardness meter, a friction and wear tester, and other equipment. Ultrasonic vibrations significantly improved the problems of pores in the coating, and the porosity was reduced from 0.13 to 0.014%. When the vibration frequency was 32 kHz in the experiment, the aspect ratio of the coating was optimized from 2.06 to 2.48, the dilution rate increased from 5.60 to 5.79%, the hardness increased from 960.25 to 988.45 HZ1.0, and the friction coefficient was reduced from 0.34 to 0.27. The coating performance was significantly improved, and the research results provide a reference for preparing excellent Ni60/WC-TiC+La2O3 composite coating.