The roles of sub‐micron and microscale roughness on shear‐driven thrombosis on titanium alloy surfaces

Background Continuous‐flow ventricular assist devices (cfVADs) are implanted in patients with end‐stage heart failure to assist with blood circulation. However, VAD implantation is associated with dangerous thrombotic complications. Our goal was to determine the impact of micron and sub‐micron scale Ti6Al4V surface roughness on adherent platelet aggregate properties under clinically relevant shear rates. Methods We used fluorescence microscopy to visualize platelets in real time as they adhered to Ti6Al4V coupons of varying degrees of roughness, including a smooth control, in microfluidic channels and quantified deposition using an image processing algorithm. We systematically characterized roughness using spatial frequencies to generalize results for more blood‐biomaterial contact applications. Results We observed that on the control and sub‐micron rough surfaces, at 1000 s−1, platelets adhered uniformly on the surface. At 2000 s−1, we observed small and stably adherent platelet aggregates. At 5500 s−1, platelet aggregates were large, unstable and interconnected via fibrillar structures. On a surface with micron‐scale roughness features, at all three shear rates, platelets deposited in the troughs of the roughened surface, and formed aggregates. Thrombus height at 2000 s−1 and 5500 s−1 was greatest on the roughest surface and lowest on the mirror‐finished surface, as indicated by the mean fluorescence intensity. Conclusions These results demonstrated that at high shear rates, thrombi form regardless of surface topography at the scales applied. At lower shear rates, micron‐scale surface features cause thrombus formation, whereas submicron features result in innocuous platelet adhesion. These findings have implications for manufacturing costs and other considerations. Our goal was to determine the impact of surface roughness on platelet aggregate properties under clinically relevant shear rates. We used fluorescence microscopy to quantify platelet adhesion on roughened Ti6Al4V surfaces in microfluidic channels and quantified deposition using an image processing algorithm. Our results demonstrated that at high shear rates, thrombi form regardless of surface topography at the scales applied, whereas at lower shear rates, micron‐scale surface features cause thrombus formation, whereas submicron features result in innocuous platelet adhesion.