Boosting brackish water treatment via integration of mesoporous γ-Al 2 O 3 NPs with thin-film nanofiltration membranes

In this study, a simple method based on non-ionic surfactant polysorbates-80 was used to create mesoporous γ-Al O NPs. The properties of the prepared mesoporous alumina nanoparticles (Al O NPs) were verified using ATR-FTIR, XRD, SEM, TEM, DLS, and BET surface area analysis. Then, thin-film nanocomposite (TFN) nanofiltration membranes were fabricated by interfacial polymerization of embedded polyamide layers with varied contents (0.01 to 0.15 wt.%) of mesoporous γ-Al O NPs. The surface roughness, porosity, pore size, and contact angle parameters of all the prepared membranes were also determined. The performance of the fabricated membranes was investigated under various mesoporous γ-Al O NPs loads, time, and pressure conditions. Mesoporous γ-Al O NPs revealed an important role in raising both the membrane hydrophilicity and the surface negativity. The addition of 0.03 wt.% mesoporous γ-Al O NPs to the TFN membrane increased water flux threefold compared to the TF control (TFC) membrane, with maximum water flux reaching 96.5, 98, 60, and 52 L/(m .h) for MgSO , MgCl , Na SO , and NaCl influent solutions, respectively, with the highest salt rejection of 96.5%, 92.2%, 98.4%. The TFN-Al O membrane was also able to soften water and remove polyvalent cations such as Mg with a highly permeable flux. The TFN-Al O membrane successfully removed the hardness of the applied water samples below the WHO limit compared to using merely the TFC membrane. Furthermore, the TFN-Al O nanofiltration membrane unit proved to be a promising candidate for the desalination of real brine like that collected from the Safaga area, Egypt.