Enhancement of mechanical strength of TCP-alginate based bioprinted constructs

To overcome the mechanical drawback of bioink, we proposed a supporter model to enhance the mechanical strength of bioprinted 3D constructs, in which a unit-assembly idea was involved. Based on Computed Tomography images of critical-sized rabbit bone defect, the 3D re-construction was accomplished by a sequenced process using Mimics 17.0, BioCAM and BioCAD software. 3D constructs were bioprinted using polycaprolactone (PCL) ink for the outer supporter under extrusion mode, and cell-laden tricalcium phosphate (TCP)/alginate bioink for the inner filler under air pressure dispensing mode. The relationship of viscosity of bioinks, 3D bioprinting pressure, TCP/alginate ratio and cell survival were investigated by the shear viscosities analysis, live/dead cell test and cell-counting kit 8 measurement. The viscosity of bioinks at 1.0 s−1-shear rate could be adjusted within the range of 1.75 ± 0.29 Pa·s to 155.65 ± 10.86 Pa·s by changing alginate concentration, corresponding to 10 kPa–130 kPa of printing pressure. This design with PCL supporter could significantly enhance the compressive strength and compressive modulus of standardized 3D mechanical testing specimens up to 2.15 ± 0.14 MPa to 2.58 ± 0.09 MPa, and 42.83 ± 4.75 MPa to 53.12 ± 1.19 MPa, respectively. Cells could maintain the high viability (over 80%) under the given printing pressure but cell viability declined with the increase of TCP content. Cell survival after experiencing 7 days of cell culture could be achieved when the ratio of TCP/alginate was 1 : 4. All data supported the feasibility of the supporter and unit-assembly model to enhance mechanical properties of bioprinted 3D constructs. [Display omitted] •A supporter and unit-assembly model enhanced mechanical property of 3D mechanical testing specimens.•PCL supporter contributed to the mechanical improvement, suitable for hard-tissue.•Rheological properties of bioink directly affected cells viability during bioprinting.