Influence of electrospun Nylon 6,6 nanofibrous mats on the interlaminar properties of Gr–epoxy composite laminates

► In this work electrospun nanofibers are interleaved in composite laminates. ► Virgin and nanomodified laminates are tested under Mode I and Mode II conditions. ► AE technique is used to investigate laminate behavior. ► Test results demonstrate that a nanofibrous mat enhances mechanical properties. ► AE analysis confirm that nanofibers are able to mitigate crack onset and propagation. The present work aims at investigating the influence of electrospun Nylon 6,6 nanofibrous mat to interlaminar strength. Mode I and the Mode II fracture mechanics of virgin and nanomodified laminates are investigated. Nanomodified laminates are fabricated by interleaving an electrospun nanofibrous mats in laminate mid-plane. Double Cantilever Beam (DCB) and End Notched Flexure (ENF) tests are performed on both virgin and nanomodified configuration. Results show that electrospun nanofibrous mat is able to increase by 23.2% the mechanical energy absorbing capability and by about 5% the G IC . ENF tests reveal that the nanofibrous mats contribute to improve the maximum stress before the material crisis (6.5% of increment) and a measurable increment of (8.1%) the maximum mechanical energy that can be absorbed by the material during the crack propagation is registered. The acoustic emission (AE) technique is used to monitor both DCB and ENF tests. The AE information highlight that the nanofibrous mats mitigate the interlaminar matrix failure on both the fracture modes.