Piezoelectric and dielectric characteristics of low temperature sintering Pb(Ni sub(1/3)Nb sub(2/3))O sub( 3)-Pb(Mn sub(1/3)Nb sub(2/3) )O sub(3)-Pb(Zr sub(1/2) Ti sub(1/2))O sub(3) ceramics for multilayer piezoelectric actuator

In this study, in order to develop the composition ceramics for multilayer piezoelectric actuator, PNN substituted PMN-PZT ceramics were fabricated using Li sub(2)CO sub(3) and Na sub(2)CO sub(3) as sintering aids, and their piezoelectric and dielectric characteristics were investigated. With the increase of the amount of PNN substitution, dielectric constant ( epsilon r), electromechanical coupling factor (k sub(p)), and piezoelectric constant (d sub(33)) of specimens showed the maximum value at each sintering temperature, and crystal structure changed from tetragonal to rhombohedral. At the sintering temperature of 950 super()C, the density, epsilon r, k sub(p), d sub(33), Q sub(m) and Tc of 12 mol% PNN substituted PMN-PNN-PZT composition ceramics showed the optimal values of 7.79 g/cm super(3), 1160, 0.599, 419pC/N, 894 and 332 super()C, respectively, for low loss multilayer piezoelectric actuator application.