effect of polyethylene addition on the morphology of polystyrene/polyamide blends

The effect of a small admixture of high-density polyethylene (HDPE) with a high or low viscosity to polystyrene/polyamide (PS/PA) blends of various compositions was studied. PS/PA blends with composition near 50/50 form sheet-like or fiber-like morphology at mixing that passes to the cocontinuous structure during compression molding. Ternary PS/PA/HDPE blends with PS/PA ratio about 50/50 show similar behavior. Generally, neither continuity nor shape of PS and PA phases was changed qualitatively by the addition of a small amount of HDPE. In agreement with existing rules for ternary blends, HDPE particles prefer a contact with PS phase to PA phase. On the other hand, none of these rules explains why a number of small HDPE subinclusions were dispersed into PS particles instead of HDPE-PS core-shell structure with a lower Gibbs free energy. Quantitative evaluation of the size of PA particles in blends with PS matrix showed that the previously proposed rule stating, that the addition of a small amount of a third immiscible component leads to a strong decrease in the size of dispersed particles, was not valid for the blends studied in this work.