Particle size effect on the permeability properties of nano-SiO sub(2) blended Portland cement concrete

In this study, nano-SiO sub(2) has been used as a high reactive pozzolan to develop the microstructure of the interfacial transition zone between the cement paste and the aggregate. Mechanical tests of blended cement-based concretes exposed that in addition of the pozzolanic reactivity of nano-SiO sub(2) (chemical aspect), its particle grading (physical aspect) also revealed considerable influences on the blending effectiveness. It was concluded that the relative permeability reduction (relative to the control concrete made with plain cement) is higher for coarser nano-SiO sub(2) after 90 days of moisture curing. However, finer nano-SiO sub(2) particles showed better effects in early ages. These phenomena can be due to the free spacing between mixture particles that was associated with the global permeability of the blended cement-based concretes. This article presents the results of the effects of particle size ranges involved in nano-SiO sub(2) blended Portland cement on the water permeability of concrete. It is revealed that the favorable results for coarser nano-SiO sub(2) reflect enhanced particle packing formation accompanied by a reduction in porosity and particularly in particle spacing after 90 days.