Effect of Connector Design on Fracture Resistance of Zirconia All-ceramic Fixed Partial Dentures
The purpose of the present study was to determine the relationship between cross-sectional design and fracture load using a static load bearing test in yttria-stabilized tetragonal zirconia polycrystal ceramic frameworks on a molar fixed partial denture. The test framework was designed as a 3-unit b...
Gespeichert in:
Veröffentlicht in: | Bulletin of Tokyo Dental College 2011, Vol.52(2), pp.61-67 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The purpose of the present study was to determine the relationship between cross-sectional design and fracture load using a static load bearing test in yttria-stabilized tetragonal zirconia polycrystal ceramic frameworks on a molar fixed partial denture. The test framework was designed as a 3-unit bridge with two abutment teeth at the second premolar and second molar of the mandible. The cross-sectional area of the connector was 9.0, 7.0, or 5.0mm2. In terms of shape, the cross-section was either circular or oval, with a height/width ratio of 1:1, 3:4, or 2:3. For each of the 9 combinations of cross-sectional area and shape, 5 frameworks were prepared (45 in total). Frameworks were cemented to a metallic test model with adhesive resin cement. After fracture load was measured, the percentage of fracture sites was determined and the fracture surfaces observed. In terms of cross-sectional area, there was a statistically significant difference in fracture load between 9.0, 7.0, and 5.0mm2. No significant difference in fracture load was observed between any two shapes of connector (p>0.05). The fracture load of all frameworks with a cross-sectional area of 9.0 or 7.0mm2 was over 880 N, which was recognized as parafunctional occlusal force. Fracture occurred at the distal connector in 82.2% of all frameworks on average. Fracture load decreased as cross-sectional area of the connector became smaller. The cross-sectional shape used in the present study was less influential on fracture load. It appears to be clinical possible to apply a connector with a cross-sectional area of 7.0mm2. Fracture often occurred at the distal connector between the pontic and the abutment, corresponding to the second molar. |
---|---|
ISSN: | 0040-8891 |
DOI: | 10.2209/tdcpublication.52.61 |