Fabrication of SmCo 5 -CrTa Granular Films

A Sm-Co-CrTa granular layer between a Sm-Co continuous layer and a Cu underlayer was prepared in order to improve magnetic properties and magnetic reversal process of Sm-Co perpendicular film. A phase of CrTa alloy in Sm-Co-CrTa layer has a role in control of Cu partial interlayer diffusion between the Sm-Co continuous layer and the Cu underlayer. The Cu diffusion provides the partial crystallization of SmCo 5 in the continuous layer. Although the perpendicular coercivity of films decreased slightly by introducing the CrTa alloy into Sm-Co layer, the magnetic intergranular exchange interaction in the films was drastically improved. Size of average magnetic cluster became smaller and magnetization reversal process was changed from a wall-motion to a coherent rotation for increasing the thickness ratio of Sm-Co-CrTa/Sm-Co layers. We confirmed that an addition of Sm-Co-CrTa layer is effective to reduce the intergranular exchange interaction in Sm-Co perpendicular films without deterioration of perpendicular magnetic anisotropy.