Structural and magnetic study of swift heavy ion irradiated W/Fe multilayer structure

The present study reports the effect of swift heavy ion irradiation on structural and magnetic properties of sputtered W/Fe multilayer structure (MLS) having bilayer compositions of [W(10 Å)/Fe(20 Å)] 10BL. The MLS is irradiated by 120 MeV Au 9+ ions of fluences 1×10 13 and 4×10 13 ions/cm 2. Techniques like X-ray reflectivity (XRR), cross-sectional transmission electron microscopy (X-TEM) and DC magnetization with a vibrating sample magnetometer (VSM) are used for structural and magnetic characterization of pristine and irradiated MLS. Analysis of XRR data using Parratt’s formalism shows a significant increase in W/Fe layer roughness. X-TEM studies reveal that intra-layer microstructure of Fe layers in MLS becomes nano-crystalline on irradiation. DC magnetization study shows that with spacer layer thickness interlayer coupling changes between ferromagnetic to antiferromagnetic.