The effect of particle size on the characteristics of FeCo nanoparticles

Some size-dependent characteristics of FeCo nanoparticles are investigated in this paper. The nanoparticles are fabricated using a coprecipitation route and their sizes are controlled by changing the reaction time. Transverse electron microscopy (TEM) images show that the nanoparticles are all spher...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Solid state communications 2010-04, Vol.150 (13), p.594-597
Hauptverfasser: Hesani, M., Yazdani, A., Abedi Ravan, B., Ghazanfari, M.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Some size-dependent characteristics of FeCo nanoparticles are investigated in this paper. The nanoparticles are fabricated using a coprecipitation route and their sizes are controlled by changing the reaction time. Transverse electron microscopy (TEM) images show that the nanoparticles are all spherical with an average size of 2–6 nm. The average size obtained from X-ray diffraction (XRD) measurements is in the range 1–3 nm. Magnetic measurements reveal that the nanoparticles are ordered ferromagnetically and have a high coercivity of about 500 Oe. In our measurements, the coercivity was decreased with decreasing particle size, indicating that the nanoparticles were in a single-domain region. Production of FeCo nanoparticles with high coercivity and fine dimension is highly promising for future recording media technology.
ISSN:0038-1098
1879-2766
DOI:10.1016/j.ssc.2009.12.043