Mixture of LiBF sub(4) and lithium difluoro(oxalato)borate for application as a new electrolyte for lithium-ion batteries

An equimolar mixture of fluoroborate salts: LiBF sub(4) and lithium difluoro(oxalate)borate LiBF sub(2)(C sub(2)O sub(4)) (MIX-LiFBs) was obtained from a simple one-step reaction of lithium oxalate and boron fluoride. Voltamperommetry shows that the salt obtained is stable in the potential range of 4.9 V. Impedance measurements of liquid electrolytes involving imidazolium ionic liquid and aliphatic carbonates have been carried out, which show the highest ionic conductivity of the order of 10 super(-3) S cm super(-1) (and low activation energy of 0.14 eV) when using carbonates as the solvent. The mixture of fluoroborate salts MIX-LiFBs used as a component of solid polymer electrolytes provides much higher ionic conductivity values at high salt concentrations in "polymer-in-salt systems". The conductivity of solid polymer electrolytes was considerably increased by adding a low-molecular-weight organic plasticizer.