Soft-Chemical Exfoliation Route to Layered Cobalt Oxide Monolayers and Its Application for Film Deposition and Nanoparticle Synthesis

A colloidal suspension of exfoliated, layered cobalt oxide nanosheets has been synthesized through the intercalation of quaternary tetramethylammonium ions into protonated lithium cobalt oxide. According to atomic force microscopy, exfoliated nanosheets of layered cobalt oxide show a plateau‐like height profile with nanometer‐level height, underscoring the formation of unilamellar 2D nanosheets. The exfoliation of layered cobalt oxide was cross‐confirmed by X‐ray diffraction, UV/Vis spectroscopy, and transmission electron microscopy. The maintenance of the hexagonal in‐plane structure of the cobalt oxide lattice after the exfoliation process was evidenced by selected‐area electron diffraction and Co K‐edge X‐ray absorption near‐edge structure analysis. The zeta‐potential measurements clearly demonstrated the negative surface charge of cobalt oxide nanosheets. Adopting the nanosheets of layered cobalt oxide as a precursor, we were able to prepare the monodisperse CoO nanocrystals with a particle size of ≈10 nm as well as the heterolayered film composed of cobalt oxide monolayer and polycation. Layered CoO2 nanosheets: Exfoliated nanosheets of layered cobalt oxide can be synthesized through the intercalation of quaternary tetramethylammonium ions into protonated lithium cobalt oxide. The hexagonal lattice of layered cobalt oxide remains intact even after the exfoliation process (see scheme). Through the deposition of colloidal suspension, we can produce monodisperse cobalt oxide nanoparticles as well as the monolayer film of cobalt oxide.