Evaluation of titanium plasma-sprayed and plasma-sprayed hydroxyapatite implants in vivo

In this study, bone interfacial strength and bone contact length at the plasma-sprayed hydroxyapatite (HA) and titanium plasma-sprayed (TPS) implants were evaluated in vivo. Non-coated titanium (Ti) implants were used as controls. Cylindrical coated or non-coated implants (4.0 mm diameter by 8 mm lo...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Biomaterials 2004-08, Vol.25 (19), p.4601-4606
Hauptverfasser: Ong, Joo L., Carnes, David L., Bessho, Kazuhisa
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In this study, bone interfacial strength and bone contact length at the plasma-sprayed hydroxyapatite (HA) and titanium plasma-sprayed (TPS) implants were evaluated in vivo. Non-coated titanium (Ti) implants were used as controls. Cylindrical coated or non-coated implants (4.0 mm diameter by 8 mm long) were implanted in the dogs’ mandibles. Loading of the implants was performed at 12 weeks after implantation. At 12 weeks after implantation (prior to loading) and 1 year after loading, implants were evaluated for interfacial bone–implant strength and bone–implant contact length. No significant differences in interfacial bone–implant strength for all groups at 12 weeks after implantation and after 1 year loading in normal bone were found. However, bone contact length for HA implants was significantly higher than the TPS and Ti implants for both periods tested (12 weeks after implantation and 1 year after loading). It was concluded that TPS implants exhibited similar pull-out strength compared to the HA implants. In addition, the lower bone contact length on the TPS surface compared to HA surfaces did not affect the interfacial bone–implant strength for both implants.
ISSN:0142-9612
1878-5905
DOI:10.1016/j.biomaterials.2003.11.053