The influence of C-factor, flexural modulus and viscous flow on gap formation in resin composite restorations

This study analyzed the influence of C-factor, flexural modulus and viscous flow on gap formation in resin composite restorations. Two resin composites, a mini-filled hybrid (P 60) and a nanofilled (Supreme), were used. The flexural modulus was obtained from bar-shaped specimens submitted to three-p...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Operative dentistry 2007-07, Vol.32 (4), p.356-362
Hauptverfasser: Moreira da Silva, Eduardo, dos Santos, Gustavo Oliveira, Guimarães, José Guilherme Antunes, Barcellos, Alexandre de Araújo Lima, Sampaio, Edwardo Martins
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:This study analyzed the influence of C-factor, flexural modulus and viscous flow on gap formation in resin composite restorations. Two resin composites, a mini-filled hybrid (P 60) and a nanofilled (Supreme), were used. The flexural modulus was obtained from bar-shaped specimens submitted to three-point bending. Viscous flow was obtained from the difference between the initial and final diameter of resin composite disks submitted to a load of 10 N for 120 seconds. Gap analysis was conducted in three types of cylindrical cavities (C-factor of 1.8, 2.6 and 3.4) that were prepared on the occlusal surfaces of human molars. The gap width at the dentin-resin composite interface was measured using a 3D scanning system (Talyscan 150). The data were analyzed by ANOVA and Student-Newman-Keuls' test, t-test and linear regression analysis (alpha = 0.05). The cavities with C-factor 3.4 presented the highest Gap formation (p < 0.0001). The lowest Gap formation was found in cavities restored with Supreme resin composite (p < 0.0001). P 60 presented significantly higher flexural modulus and lower viscous flow than Supreme (p < 0.0001). Regression analyses detected a significant influence of flexural modulus and viscous flow on gap formation (p < 0.05).
ISSN:0361-7734
1559-2863
DOI:10.2341/06-104