Silica coating of silver nanoparticles using a modified Stöber method

Silver nanoparticles prepared through a borohydride-reduction method were directly coated with silica by means of a seeded polymerization technique based on the Stöber method. Various amine catalysts were used for initialization of a sol–gel reaction of TEOS with no need for a prior surface modification. Use of dimethylamine (DMA) as a catalyst was found to be necessary to obtain a proper coating. The silica shell thickness was varied from 28 to 76 nm for TEOS concentrations of 1–15 mM at 11.1 M water and 0.8 M DMA. The optical spectra of the core–shell silver–silica composite particles show a qualitative agreement with predictions by Mie theory.