Stress gradients in titanium nitride thin films

Titanium nitride films, as used for hard coatings, were deposited on silicon wafers by reactive unbalanced magnetron sputtering. For thinner films we find a higher compressive average residual stress than for thicker films. In the paper it is shown that this reduction in average stress is not due to...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Surface & coatings technology 2008-12, Vol.203 (5), p.550-553
Hauptverfasser: Machunze, R., Janssen, G.C.A.M.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Titanium nitride films, as used for hard coatings, were deposited on silicon wafers by reactive unbalanced magnetron sputtering. For thinner films we find a higher compressive average residual stress than for thicker films. In the paper it is shown that this reduction in average stress is not due to relaxation, but to a stress gradient in the film. Experiments in which the film thickness was reduced in steps by wet chemical etching show a stress gradient present in the films. Releasing the films from the wafer, by etching away the silicon, results in bent film flakes. The flakes' bending is close to the bending calculated from the measured stress gradient, proving once more the existence of a stress gradient.
ISSN:0257-8972
1879-3347
DOI:10.1016/j.surfcoat.2008.05.005