High surface area titania photocatalytic microfluidic reactors

In this work a simple method is described for depositing a robust yet highly porous film of anatase titania nanoparticles with a very high surface area onto the inside walls of microfluidic devices. A very high loading of 66 g of titania per liter of reactant solution was achieved. The effectiveness...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:AIChE journal 2007-03, Vol.53 (3), p.695-702
Hauptverfasser: Lindstrom, Henrik, Wootton, Robert, Iles, Alexander
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In this work a simple method is described for depositing a robust yet highly porous film of anatase titania nanoparticles with a very high surface area onto the inside walls of microfluidic devices. A very high loading of 66 g of titania per liter of reactant solution was achieved. The effectiveness is demonstrated of this deposition method by producing functionalized microfluidic reactor devices and using them to photocatalytically degrade air‐saturated methylene blue solutions. Experiments were performed with and without the addition of gaseous oxygen to the microreactors. The addition of oxygen dramatically enhanced the degradation rate. This highlights the necessity for supplying additional oxygen to microsystems during photocatalysis since dissolved oxygen can be rapidly depleted within the small confined space inside microreactors. With additional gaseous oxygen, the conversion rate for the photodegradation reaction of 0.1mM methylene blue at a flow rate of 12 μl min−1 was 10.6 % s−1. © 2007 American Institute of Chemical Engineers AIChE J, 2007
ISSN:0001-1541
1547-5905
DOI:10.1002/aic.11096