Preparation and properties of polymer/LDH nanocomposite used for UV curing coatings

The thermal and mechanical properties of UV curing coatings consisted of urethane acrylates as an oligomer and a diacrylate monomer were reinforced by using layered double hydroxide (LDH). The LDH was organically modified by an ion-exchange process, in which the nitrate anions were replaced by long alkyl sulfate anions. With organic modification, the d-spacing of inorganic LDH layers was greatly enlarged to 2.75 from 0.78 nm, leading the LDH to be organophilic. During in situ photopolymerization process, the d-spacing of LDH layers was further enlarged to 4.29 nm, indicating the intercalation of polymer chains. For comparison, polymer/LDH nanocomposite filled with un-modified LDH was also prepared, and showed less enhancement in thermal and mechanical properties.