Synthesis of Nanohole‐Structured Single‐Crystalline Platinum Nanosheets Using Surfactant‐Liquid‐Crystals and their Electrochemical Characterization

Nanohole‐structured single‐crystalline Pt nanosheets have been synthesized by the borohydride reduction of Na2PtCl6 confined to the lyotropic liquid crystals (LLCs) of polyoxyethylene (20) sorbitan monooleate (Tween 80) with or without nonaethylene‐glycol (C12EO9). The Pt nanosheets of around 4–10 nm in central thickness and up to 500 nm or above in diameter have a number of hexagonal‐shaped nanoholes ∼1.8 nm wide. High‐resolution electron microscope images of the nanosheets showed atomic fringes with a spacing of 0.22 nm indicating that the nanosheets are crystallographically continuous through the nanoholed and non‐holed areas. The inner‐angle distributions for the hexagonal nanoholes indicate that the six sides of the nanoholes are walled with each two Pt (111), Pt (1${\bar {1}}$1) and Pt (010) planes. The formation mechanism of nanoholed Pt nanosheets is discussed on the basis of structural and compositional data for the resulting solids and their precursory LLCs, with the aid of similar nanohole growth observed for a Tween 80 free but oleic acid‐incorporated system. It is also demonstrated that the nanoholed Pt nanostructures loaded on carbon exhibit fairly high electrocatalytic activity for oxygen reduction reaction and a high performance as a cathode material for polymer‐electrolyte fuel cells, along with their extremely high thermostability revealed through the effect of electron‐irradiation. Nanohole‐structured platinum nanosheets with nanoholes of ∼1.8 nm wide are synthesized by the borohydride reduction of Pt salts in the lyotropic liquid crystals of polyoxyethylene (20) sorbitan monooleate (Tween 80) mixed with or without nonaethyleneglycol monododecylether (C12EO9) to demonstrate a fairly high performance as an electrocatalyst for oxygen reduction reaction or a cathode material for polymer electrolyte fuel cells.