Effect of the composition of α-MSAN copolymer on the miscibility of PVC/α-MSAN blends

A series of α-methylstyrene, styrene, and acrylonitrile (α-MSAN) copolymers with different acrylonitrile (AN) contents were synthesized by altering α-MSt, St, and AN ratios with emulsion copolymerization method. By melt-blending these copolymers with PVC resin and di-isooctyl phthalate (DOP), PVC/α-MSAN, and PVC/α-MSAN/DOP blends were prepared. The miscibility and morphology of the blends were investigated by dynamic mechanical analysis (DMA) and scanning electron microscopy. The PVC is immiscible with SAN by melt-mixing, whereas PVC is miscible with α-MSAN (α-MSt/St = 1/1) if AN weight percent is within the window range of 20-25 wt %, and α-MSAN (not containing St) with 35 wt % AN is miscible with PVC even when they are blended by melt-mixing. Replacement of styrene with α-methylstyrene widens the miscibility window with PVC. The miscibility of PVC/α-MSAN blends is substantially improved with the increasing α-MSt content in α-MSAN copolymer containing identical AN content. When DOP was introduced into the PVC/α-MSAN (α-MSt/St = 1/1) blends, a single tan δ peak over room temperature in DMA detection is found as AN content in α-MSAN copolymer is within the range of 15-25 wt %, and SEM observation also shows that the blends are homogeneous. When the AN content in α-MSAN copolymer is over 35 wt %, the presence of DOP causes the phase domain extended. The phase domain size of the PVC/α-MSAN/DOP blends intensively depends on AN content in α-MSAN copolymer.