Statistical evaluation of the strength of wear-resistant hard coatings
Strength of physically vapor deposited (PVD) titanium nitride (TiN) coating was characterized by bending test of free-standing film. By solving an inverse problem to optimize the distribution of equivalent cracks with respect to the failure probability of specimens, strength of unit surface areas wa...
Gespeichert in:
Veröffentlicht in: | Surface & coatings technology 2007-12, Vol.202 (4), p.1154-1159 |
---|---|
Hauptverfasser: | , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Strength of physically vapor deposited (PVD) titanium nitride (TiN) coating was characterized by bending test of free-standing film. By solving an inverse problem to optimize the distribution of equivalent cracks with respect to the failure probability of specimens, strength of unit surface areas was successfully evaluated. The average strength of interface side and growing side surface for the unit area of 1 μm
2 were 3.87 GPa and 2.60 GPa, respectively, which were the data first reported. |
---|---|