Continuous-Flow Synthesis of Zn1-xMnxS Nanoparticles at Ambient Conditions

With its large direct band gap and good chemical stability, ZnS is suitable for many applications, including light-emitting diodes, panel displays, and photodetection. Here, nanoparticles of ZnS are synthesized phase pure under ambient conditions by precipitation in a simple and scalable continuous-flow reactor. Furthermore, different degrees of Zn substitution with Mn have been investigated, Zn1-xMnxS, with x = 0.05, 0.19, and 0.25 according to X-ray fluorescence measurements. The products are analyzed with multitemperature synchrotron powder X-ray diffraction (PXRD) and X-ray total scattering. The analysis reveals phase-pure synthesis products with the sphalerite structure and crystallite sizes in the range of 3.8-4.7 nm in agreement with scanning transmission electron microscopy. Only Zn0.75Mn0.25S shows traces of Mn3O4, indicating that x = 0.25 is above the substitution limit as the impurity appears. Substitution of Zn with Mn in the nanoparticles is confirmed by energy-dispersive X-ray spectroscopy, as well as an observed decrease in the band gap, decrease in the sphalerite-to-wurtzite phase transition temperature, and increase in the unit cell dimensions with increasing Mn content. Based on the modeling of the PXRD Rietveld refined atomic displacement parameters, the Debye temperature for ZnS and Zn0.95Mn0.05S is determined to be 322 ± 13 and 394 ± 22 K, respectively.With its large direct band gap and good chemical stability, ZnS is suitable for many applications, including light-emitting diodes, panel displays, and photodetection. Here, nanoparticles of ZnS are synthesized phase pure under ambient conditions by precipitation in a simple and scalable continuous-flow reactor. Furthermore, different degrees of Zn substitution with Mn have been investigated, Zn1-xMnxS, with x = 0.05, 0.19, and 0.25 according to X-ray fluorescence measurements. The products are analyzed with multitemperature synchrotron powder X-ray diffraction (PXRD) and X-ray total scattering. The analysis reveals phase-pure synthesis products with the sphalerite structure and crystallite sizes in the range of 3.8-4.7 nm in agreement with scanning transmission electron microscopy. Only Zn0.75Mn0.25S shows traces of Mn3O4, indicating that x = 0.25 is above the substitution limit as the impurity appears. Substitution of Zn with Mn in the nanoparticles is confirmed by energy-dispersive X-ray spectroscopy, as well as an observed decrease in the band gap, decrease in the sphalerite-to-wurtz