Lewis-base ligand-reshaped interfacial hydrogen-bond network boosts CO2 electrolysis

Both the catalyst and electrolyte strongly impact the performance of CO2 electrolysis. Despite substantial progress in catalysts, it remains highly challenging to tailor electrolyte compositions and understand their functions at the catalyst interface. Here, we report that the ethylenediaminetetraacetic acid (EDTA) and its analogs, featuring strong Lewis acid-base interaction with metal cations, are selected as electrolyte additives to reshape the catalyst-electrolyte interface for promoting CO2 electrolysis. Mechanistic studies reveal that EDTA molecules are dynamically assembled toward interface regions in response to bias potential due to strong Lewis acid-base interaction of EDTA4–-K+. As a result, the original hydrogen-bond network among interfacial H2O is disrupted, and a hydrogen-bond gap layer at the electrified interface is established. The EDTA-reshaped K+ solvation structure promotes the protonation of *CO2 to *COOH and suppressing *H2O dissociation to *H, thereby boosting the co-electrolysis of CO2 and H2O toward carbon-based products. In particular, when 5 mM of EDTA is added into the electrolytes, the Faradaic efficiency of CO on the commercial Ag nanoparticle catalyst is increased from 57.0% to 90.0% at an industry-relevant current density of 500 mA cm−2. More importantly, the Lewis-base ligand-reshaped interface allows a range of catalysts (Ag, Zn, Pd, Bi, Sn, and Cu) to deliver substantially increased selectivity of carbon-based products in both H-type and flow-type electrolysis cells.