Stable production of hydrogen peroxide over zinc oxide @ zeolitic imidazolate Framework-8 composite catalysts

Zeolite imidazole framework −8 (ZIF-8) was used as the encapsulation layer to improve the stability and activity of ZnO nanoparticles. Under the voltage of 2.0 V vs.RHE, the stability test could be carried out for 60 h, and the yield of H2O2 did not decrease significantly. [Display omitted] A promis...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of colloid and interface science 2024-12, Vol.676, p.139-148
Hauptverfasser: Shao, Haodong, Zhang, Yue, Zhao, Jianqiang, Zhang, Chengxu, Bai, Fengning, Hu, Jue
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Zeolite imidazole framework −8 (ZIF-8) was used as the encapsulation layer to improve the stability and activity of ZnO nanoparticles. Under the voltage of 2.0 V vs.RHE, the stability test could be carried out for 60 h, and the yield of H2O2 did not decrease significantly. [Display omitted] A promising method of producing hydrogen peroxide (H2O2) is the electrochemical two-electron water oxidation reaction (2e− WOR). In this process, it is important to design electrocatalysts that are both earth abundant and environmentally friendly, as well as offering high stability and production rates. The research of WOR catalysts, such as the extensively used transition metal oxides, is mainly focused on the modification of transition metal elements. Few studies pay attention to the protective heterostructure of metal oxides. Here, we demonstrate for the first time an organometallic skeleton protection strategy to develop highly stable WOR catalysts for H2O2 generation. Unlike the pure ZnO and zeolite imidazole framework-8 (ZIF-8) catalysts, ZnO@ZIF-8 enabled the production of hydrogen peroxide at high voltages. The experimental results demonstrate that the ZnO@ZIF-8 catalyst stably generates H2O2 even under a high voltage of 3.0 V vs. RHE, with a yield reaching 2845.819 μmolmin−1 g−1. ZnO@ZIF-8 shows a relatively low overpotential, with a current density of 10 mA cm−2 and an overpotential of 110 mV. The ZnO@ZIF-8 catalyst’s maximal FE value was 4.72 %. Moreover, the ZnO@ZIF-8 catalyst exhibits remarkable durability even after an extended 60-hour stability test. Operando Raman and theoretic calculation analyses reveal that the metal–organic skeleton being encapsulated on the metal oxide surface synergizes with each other, not only expanding the electrochemical surface area, but also adjusting the catalyst metal sites’ adsorption capacity. A novel approach to the modification of 2e− WOR metal oxide catalyst is presented in this work.
ISSN:0021-9797
1095-7103
1095-7103
DOI:10.1016/j.jcis.2024.07.103