Assessments of polymerization shrinkage by optical coherence tomography-based digital image correlation analysis—Part II: Effects of restorative composites

To examine the polymerization shrinkage of different resin-based composite (RBC) restorations using optical coherence tomography (OCT) image-based digital image correlation (DIC) analysis. The refractive index (RI) of three RBCs, Filtek Z350XT (Z350), Z350Flowable (Z350F), and BulkFill Posterior (Bulkfill), was measured before and after polymerization to calibrate their axial dimensions under OCT. Class I cavities were prepared in bovine incisors and individually filled with these RBCs under nonbonded and bonded conditions. A series of OCT images of these restorations were captured during 20-s light polymerization and then input into DIC software to analyze their shrinkage behaviors. The interfacial adaptation was also examined using these OCT images. The RI of the three composites ranged from 1.52 to 1.53, and photopolymerization caused neglectable increases in the RI values. For nonbonded restorations, Z350F showed maximal vertical displacements on the top surfaces (−16.75 µm), followed by Bulkfill (−8.81 µm) and Z350 (−5.97 µm). In their bonded conditions, all showed increased displacements. High variations were observed in displacement measurements on the bottom surfaces. In the temporal analysis, the shrinkage of nonbonded Z350F and Bulkfill decelerated after 6–10 s. However, Z350 showed a rebounding upward displacement after 8.2 s. Significant interfacial gaps were found in nonbonded Z350 and Z350F restorations. The novel OCT image-based DIC analysis provided a comprehensive examination of the shrinkage behaviors and debonding of the composite restorations throughout the polymerization process. The flowable composite showed the highest shrinkage displacements. Changes in the shrinkage direction may occur in nonbonded conventional composite restorations. [Display omitted] •A novel digital image correlation analysis using OCT images was established.•Shrinkage displacements and temporal changes of three composites were examined.•Contraction behavior is affected by the type of composite and bond condition.•Nonbonded Z350 restoration showed changed shrinkage directions during curing.•Bulk-fill composite showed similar displacement maps in nonbonded and bonded conditions.