Effect of Long Glass Fiber Orientations or a Short-Fiber-Reinforced Composite on the Fracture Resistance of Endodontically Treated Premolars

This study aimed to evaluate the effect of direct restorations using unidirectional glass fiber orientations and a short-fiber-reinforced composite (SFRC) on the fracture resistance of endodontically treated premolars with mesio-occluso-distal cavities. Ninety double-rooted premolars were selected. Fifteen teeth were left intact/as a control group. The endodontic treatment and cavity preparations of seventy-five teeth were performed and divided into five experimental groups: Resin composite (RC), modified transfixed technique + RC, circumferential technique + RC, cavity floor technique + RC, and SFRC + RC. All teeth were fractured under oblique static loading at a 30° angle using a universal testing machine. The fracture patterns were observed and classified. Data were analyzed with one-way analysis of variance, Pearson chi-square, and Tukey HSD post hoc tests ( = 0.05). The highest fracture strength values were obtained in intact teeth (599.336 N), followed by modified transfixed + RC treated teeth (496.58 N), SFRC + RC treated teeth (469.62 N), RC (443.51 N), circumferential + RC treated teeth (442.835 N), and cavity floor + RC treated teeth (404.623 N) ( < 0.05). There was no significant difference between the RC and the circumferential technique + RC ( > 0.05). Unrepairable fractures were observed at low rates (20%) in the modified transfixed + RC and SFRC + RC teeth, and at higher rates in RC (73.3%), cavity floor + RC (60%), and circumferential + RC (80%) teeth. The application of an SFRC or the modified transfixed technique yielded an improved fracture strength and the fracture pattern of ETPs being restored with a universal injectable composite.