Transgranular SCC mechanism of thermally treated alloy 600 in alkaline water containing lead

This work aims to understand a SCC failure mode of thermally treated steam generator tubing materials in high temperature water containing lead. The effect of lead contents on the anodic polarization curves of alloy 600 (UNS NO6600) and alloy 690 (UNS NO6900) has been studied in a solution of pH 10 at 200 °C and 315 °C. Lead increased the active peaks of alloy 600 and alloy 690 in mild alkaline water at high temperatures. A reduction of PbO to a metallic lead in alloy 690 is easier than that of alloy 600. When lead was added into the solution, a relative ratio of Cr from among the main metallic elements (Cr, Fe, and Ni) of alloy 600 and alloy 690 decreased in the outer corrosion film. Alloy 690 TT showed a transgranular stress corrosion cracking (TGSCC) in a 10 M NaOH solution with 5000 ppm of lead. Intergranular stress corrosion racking (IGSCC) was observed in the 100 ppm lead condition, and some TGSCC was detected on the fracture surface of the alloy 600 MA cracked in the 10,000 ppm lead solution. IGSCC seemed to be retarded by a crack blunting around the grain boundaries, and the TG cracking mode of the thermally treated alloy 600 and 690 seemed to be related to a crack blunting at the grain boundary carbide and a film dissolution by lead in an alkaline solution.