Delamination Analysis of Low-Temperature Processed SU-8 Photoresist for MEMS Device Fabrication
Negative SU-8 photoresist processed at several levels of lower temperature than conventional approach was investigated, and its low-temperature processing has been characterized in terms of delamination. According to two phases of statistical design of experiment (DOE), initially statistically signi...
Gespeichert in:
Veröffentlicht in: | Key engineering materials 2007-08, Vol.345-346, p.1397-1400 |
---|---|
Hauptverfasser: | , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Negative SU-8 photoresist processed at several levels of lower temperature than
conventional approach was investigated, and its low-temperature processing has been characterized
in terms of delamination. According to two phases of statistical design of experiment (DOE), initially
statistically significant variables of SU-8 photoresist processing were selected, and the selected
variables were further investigated to find their effects on delamination of SU-8 microstructure. A
three leveled factorial designed experiments were performed followed by a 2(6-1)
fractional factorial
designed as a screening experiment. Characterizing low-temperature SU-8 photoresist process, 27
samples were fabricated and the degree of delamination was measured. In addition, nine additional
samples were fabricated for the purpose of verification. Employing a neural network modeling
technique, a process model is established, and response surfaces are generated to investigate the
degree of delamination associated with three process parameters: post exposure bake (PEB)
temperature, PEB time, and exposure energy. From the response surfaces generated, two significant
parameters associated with delamination are identified, and their effects on delamination were
analyzed. The higher the post exposure bake (PEB) temperature at a fixed PEB time and the more
delamination occurred. In addition, the higher the dose of exposure energy, the lower the temperature
at which the delamination begins and the larger the degree of delamination. The results identified
acceptable ranges of the three process variables to avoid the delamination of SU-8 film, which in turn
might lead to potential defects in MEMS device fabrication. |
---|---|