Synthesis and Characterization of Y2O3:Eu3+ Film Derived by Sol-Gel Processing

Y2O3:Eu3+ thin film was synthesized by sol-gel method with inorganic salt raw materials, and the crystal structure and luminescent properties were investigated. By adding organic additive to the sol, a homogeneous film with high luminescent intensity could be obtained by dip-coating technique on the surface of alumina sheet and quartz glass. Structures of the films were studied by XRD and SEM. The excitation spectra of the films showed a wide excitation peak from 200nm to 260nm, and the emission spectra had a strongest emission peak at 611nm which revealed a close relationship with the calcining temperature.