Effect of temperature on the pore solution, microstructure and hydration products of Portland cement pastes

The effect of temperature on the hydration products and the composition of the pore solution are investigated for two Portland cements from 5 to 50 °C. Increased temperature leads to an initially fast hydration and a high early compressive strength. At 40 and 50 °C, the formation of denser C–S–H, a more heterogeneous distribution of the hydration products, a coarser porosity, a decrease of the amount of ettringite as well as the formation of very short ettringite needles has been observed. At 50 °C, calcium monosulphoaluminate has formed at the expenses of ettringite. In addition, the amount of calcium monocarboaluminate present seems to decrease. The composition of the pore solution mirrors the faster progress of hydration at higher temperatures. After 150 days, however, the composition of the pore solution is similar for most elements at 5, 20 and 50 °C. Exceptions are the increased sulphate concentrations and the slightly lower Al and Fe concentrations at 50 °C.