Shear bond strength of orthodontic brackets bonded with primer-incorporated orthodontic adhesives and unpolymerized 3-dimensional printing materials on 3-dimensional-printed crowns

The use of 3-dimensional (3D) printing techniques in fabricating crowns has increased the demand for bracket bonding onto these surfaces. The objective was to evaluate the shear bond strength (SBS) of orthodontic brackets bonded onto 3D-printed crowns using primer-incorporated orthodontic adhesives...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:American journal of orthodontics and dentofacial orthopedics 2024-06, Vol.165 (6), p.663-670
Hauptverfasser: Choi, Yukyung, Moon, Wonjoon, Manso, Adriana P., Park, Young-Seok, Lim, Bum-Soon, Chung, Shin Hye
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The use of 3-dimensional (3D) printing techniques in fabricating crowns has increased the demand for bracket bonding onto these surfaces. The objective was to evaluate the shear bond strength (SBS) of orthodontic brackets bonded onto 3D-printed crowns using primer-incorporated orthodontic adhesives and 3D printing materials as orthodontic adhesives. A total of 160 crowns were printed with two 3D printing materials, DentaTOOTH (Asiga, Sydney, Australia) (group A) and NextDent C&B Micro Filled Hybrid (3D Systems, Soesterberg, Netherlands) (group N). Each group was randomly divided into 4 adhesive subgroups (n = 20): Transbond XT (for groups A [ATX] and N [NTX]; 3M Unitek, Monrovia, Calif), Ortho Connect (for groups A [AOC] and N [NOC]; GC Corporation., Tokyo, Japan), Orthomite LC (for groups A [AOM] and N [NOM]; Sun Medical, Co Ltd, Moriyama, Shiga, Japan), and unpolymerized liquid state of 3D printing resin (for groups A [AA] and N [NN]). SBS was measured with a universal testing machine at a crosshead speed of 0.5 mm/min. The adhesive remnant index and the mode of failure were analyzed under the microscope. Statistical analysis was performed at a significance level of α = 0.05. When used as adhesives (AA and NN), 3D printing materials showed no statistically significant difference in SBS compared with Transbond XT (ATX and NTX, respectively). In group N, NN showed a significantly higher SBS than primer-incorporated orthodontic adhesives (NOC and NOM; P 
ISSN:0889-5406
1097-6752
DOI:10.1016/j.ajodo.2024.01.013