Temperature dependence of the mechanical properties of melt-processed Dy–Ba–Cu–O bulk superconductors evaluated by three point bending tests

Dy-Ba-Cu-O bulk superconductor has an excellent capability of trapping magnetic flux and lower heat conductivity at cryogenic temperatures as compared with Y-Ba-Cu-O bulk superconductor. The Young's modulus and the bending strength in the range from room temperature to 7 K were measured by the three-point bending tests using specimens cut from a melt-processed Dy-Ba-Cu-O bulk superconductor. They were tested in a helium gas flow type cryostat at Forschungszentrum Karlsruhe and in a liquid nitrogen bath at Iwate University. The Young's modulus was calculated by either the slope of stress-strain curve or that of the load-deflection curve of the specimen. Although the bending strength measured in the two institutes coincided well, there was a significant discrepancy in the Young's modulus. The Young's modulus and bending strength increased with decrease of temperature down to 7 K. The amount of increase in the Young's modulus and the bending strength were about 32% and 36% of those at room temperature, respectively. The scatter of data for each run was significant and did not depend on temperature. The temperature dependence of the Young's modulus coincided with that in Y-Ba-Cu-O obtained by ultrasonic velocity. The temperature dependence of the Young's modulus and the bending strength was discussed from the view point of interatomic distance of the bulk crystal.