Controlled solvothermal synthesis of self-assembled SrTiO3 microstructures for expeditious solar-driven photocatalysis dye effluents degradation

In this work, the self-assembled SrTiO3 (STO) microstructures were synthesized via a facile one-step solvothermal method. As the solvothermal temperature increased from 140 °C to 200 °C, the STO changed from a flower-like architecture to finally an irregularly aggregated flake-like morphology. The photocatalytic performance of as-synthesized samples was assessed through the degradation of rhodamine B (RhB) and malachite green (MG) under simulated solar irradiation. The results indicated that the photocatalytic performance of STO samples depended on their morphology, in which the hierarchical flower-like STO synthesized at 160 °C demonstrated the highest photoactivities. The photocatalytic enhancement of STO-160 was benefited from its large surface area and mesoporous configuration, hence facilitating the presence of more reactive species and accelerating the charge separation. Moreover, the real-world practicality of STO-160 photocatalysis was examined via the real printed ink wastewater-containing RhB and MG treatment. The phytotoxicity analyses demonstrated that the photocatalytically treated wastewater increased the germination of mung bean seeds, and the good reusability of synthesized STO-160 in photodegradation reaction also promoted its application in practical scenarios. This work highlights the promising potential of tailored STO microstructures for effective environmental remediation applications. [Display omitted] •SrTiO3 microstructures were successfully prepared by a one-step solvothermal route.•Influence of solvothermal temperature on the synthesis of SrTiO3 was considered.•SrTiO3 gradually changed from flower-like shape to aggregated flake-like shape.•STO-160 showed good solar photoactivity for RhB and MG dye effluent degradation.•STO-160 showed good stability upon four successive cycles.