Uniaxial anisotropy in magnetite thin film—Magnetization studies

Magnetization and electrical resistivity measurements have been performed on a stoichiometric single crystalline magnetite Fe 3O 4 thin film (thickness of ca. 500 nm) MBE deposited on MgO (1 0 0) substrate. The aim of these studies was to check the influence of preparation method and sample form (bulk vs. thin film) on magnetic anisotropy properties in magnetite. The film magnetization along 〈0 0 1〉 versus applied magnetic field has been determined both in the direction parallel and perpendicular to the film surface, and at temperatures above and below the Verwey transition. We have found, in agreement with published results, that the in-plane field of 10 kOe was not sufficient to saturate the sample. This can be understood if some additional factor, on top of the bulk magnetocrystalline anisotropy, is taken into account.