Injection moulding of oxide reduced copper powders

Fine oxide reduced copper powders of about 10 μm mean grain size are irregular in particle shape and high in oxygen content, which poses a difficulty in achieving good properties from injection moulding. Injection moulding was possible when a multicomponent binder with a large fraction of the backbone polymer was used. Injection moulded parts could be sintered to a density of about 95% theoretical, if reduction of the residual oxides in the powder was effectively carried out prior to closure of pores during sintering. Under such a condition, the injection moulded parts could attain an electrical conductivity higher than 80% of pure copper. July 2004.