Microstructural Evolution and Mechanical Properties of Modified 9%Cr-1%Mo Steel upon Isothermal Heat-Treatment
The evolution of microstructure and its effects on the mechanical properties of modified 9%Cr-1%Mo steel during heat-treating at 1050°C for 15 min and then isothermal heat treatment at 380~760°C with subsequent air-cooling have been investigated. For the microstructural and mechanical property analy...
Gespeichert in:
Veröffentlicht in: | Materials science forum 2005-01, Vol.475-479, p.81-84 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The evolution of microstructure and its effects on the mechanical properties of modified 9%Cr-1%Mo steel during heat-treating at 1050°C for 15 min and then isothermal heat treatment at 380~760°C with subsequent air-cooling have been investigated. For the microstructural and mechanical property analyses, OM, SEM, EDS, XRD, hardness and impact tests were used. In accordance with the severity of the heat-treatment, the microstructure evolved from the untransformed martensite to the partially transformed dual phases of martensite and ferrite, and then fully transformed to ferrite. Impact values at ambient temperature for specimens isothermally heat-treated at 320 - 380°C, predominantly at about 350°C were lower than others’ with similar martensitic structure. The partially transformed specimens with dual phases of martensite and ferrite also showed lower impact values than samples with untransformed with martensitic, and transformed with ferritic structures. |
---|---|
ISSN: | 0255-5476 1662-9752 1662-9752 |
DOI: | 10.4028/www.scientific.net/MSF.475-479.81 |