Chitosan-Stabilized CuO Nanostructure-Functionalized UV-Crosslinked PVA/Chitosan Electrospun Membrane as Enhanced Wound Dressing

Electrospun nanofibrous membranes are of great interest for tissue engineering, active material delivery, and wound dressing. These nanofibers possess unique three-dimensional (3D) interconnected porous structures that result in a higher surface-area-to-volume ratio and porosity. This study was carried out to prepare nanofibrous membranes by electrospinning a blend of PVA/chitosan polymeric solution functionalized with different ratios of copper oxide. Chitosan-stabilized CuO nanoparticles (CH-CuO NPs) were biosynthesized successfully utilizing chitosan as the capping and reducing agent. XRD analysis confirmed the monoclinic structure of CH-CuO NPs. In addition, the electrospun nanofibrous membranes were UV-crosslinked for a definite time. The membranes containing CH-CuO NPs were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), Fourier transform infrared (FTIR) spectroscopy, ultraviolet–visible (UV–vis) spectrophotometry, and dynamic light scattering (DLS). SEM results showed the nanosize of the fiber diameter in the range of 147–207 nm. The FTIR spectroscopy results indicated the successful incorporation of CH-CuO NPs into the PVA/chitosan nanofibrous membranes. DSC analysis proved the enhanced thermal stability of the nanofibrous membranes due to UV-crosslinking. Swelling and degradation tests were carried out to ensure membrane stability. Greater antimicrobial activity was observed in the nanoparticle-loaded membrane. An in vitro release study of Cu2+ ions from the membrane was carried out for 24 h. The cytotoxicity of CH-CuO NP-incorporated membranes was investigated to estimate the safe dose of nanoparticles. An in vivo test using the CH-CuO NP-loaded PVA/chitosan membrane was conducted on a mice model, in which wound healing occurred in approximately 12 days. These results confirmed that the biocompatible, nontoxic nanofibrous membranes are ideal for wound-dressing applications.